Analysis of the distribution of microhardness, mineral, and organic content of human, bovine, and ovine teeth / Análisis de la distribución de microdureza, contenido mineral y orgánico de dientes humanos, bovinos y ovinos

Objetive. Human teeth have been commonly used for in vitro and in situ studies. Cu­rrently, other animals' teeth have been purposed for dental research to overcome human teeth' problematic availability. This study aimed to investigate the enamel and dentin from human, bovine, and ovine teeth concerning the microhardness, organic, and in­ organic contents via micro­Raman spectroscopy. Methods. Human, bovine, and ovine teeth were divided according to their type and age into seven groups: Ovine; Bovine­12 months; Bovine­24 months; Bovine­36 months; Bovine­48 months; Bovine­+60 months; Human (control). The enamel's microhardness (superficial and deep) and den­tin (superficial, middle, and deep) were analyzed. The calcium/phosphate ratio and am­ide contents were determined by micro­Raman spectroscopy. Results. Overall, the mi­crohardness of human enamel was superior to the other species. Dentin's microhardness was similar among groups. Ovine group showed lower values of calcium/phosphate ratio than human. Amide content was similar between bovine and human. The microhardness and calcium/phosphate ratio of enamel and dentin, respectively, decreased as the age of bovine teeth increased. Conclusions. Researchers must be aware and take into consider­ation the differences of ovine and bovine enamel compared to human enamel. Other al­ternatives that are more similar to the microhardness of human enamel should be sought. Bovine teeth of 12 and 24 months are suitable substitutes for dentin of human teeth. Researchers must also be aware of the age of the animals and specify it in the studies.

Objetivo. Los dientes humanos se han utilizado comúnmente para estudios in vitro e in situ. Actualmente, los dientes de otros animales se han destinado a la investiga­ción dental para superar la disponibilidad problemática de los dientes humanos. Este estudio tuvo como objetivo investigar el esmalte y la dentina de los dientes humanos, bovinos y ovinos en relación con la microdureza y los contenidos orgánicos e inor­gánicos a través de la espectroscopia micro­Raman. Métodos. Los dientes humanos, bovinos y ovinos se dividieron según su tipo y edad en siete grupos: Ovinos; Bovino­12 meses; Bovino­24 meses; Bovino­36 meses; Bovino­48 meses; Bovino­+60 meses; Hu­mano (control). Se analizó la microdureza del esmalte (superficial y profunda) y de la dentina (superficial, media y profunda). La relación calcio/fosfato y los contenidos de amida se determinaron mediante espectroscopía micro­Raman. Resultados. En general, la microdureza del esmalte humano fue superior a la de otras especies. La microdureza de la dentina fue similar entre los grupos. El grupo ovino mostró valores más bajos de la relación calcio/fosfato que el humano. El contenido de amida fue similar entre bovinos y humanos. La microdureza y la relación calcio/fosfato del esmalte y la dentina, respectiva­mente, disminuyeron a medida que aumentaba la edad de los dientes bovinos. Conclusiones. El esmalte de los dientes ovinos y bovinos no es un sustituto adecuado del de los dientes humanos. Se deben buscar otras alternativas que sean similares a la microdureza del esmalte humano. Sin embargo, los dientes bovinos de 12 y 24 meses son sustitutos adecuados de la dentina de los dientes humanos. Los investigadores deben conocer la edad de los animales y especificarla en los estudios.

Bone formation in sinus augmentation with different xenograft particle sizes: systematic review and meta-analysis / Formação óssea em levantamento de seio maxilar com diferentes tamanhos de partículas de enxerto xenográfico: revisão sistemática e meta-análise

ABSTRACT The commercial bovine bone mineral most commonly used is available in two particle sizes and studies have demonstrated contradictory results regarding bone formation volume using small or large particles. The aim of this systematic review and meta-analysis was to compare the bone formation volume and residual bovine bone volume in sinus floor augmentation using small and large particles. The following outcome measures were assessed: bone formation volume (%) and residual bovine bone particles volume (%) assessed by histomorphometric analysis. The initial screening resulted in 236 records. After removal of duplicated articles and analysis of titles, abstracts and full texts, three articles were included in the meta-analysis. The bone formation volume and residual bovine bone volume did not differ between small and large particles, with low heterogeneity of studies. The particle size of bovine bone mineral did not influence bone formation percentage; small and large particles of bovine bone graft presented similar residual bone mineral; more randomized clinical trials should be performed to completely confirm that bovine bone mineral particle size does not affect the result of sinus floor augmentation.

RESUMO O enxerto ósseo bovino comercial mais comumente utilizado está disponível em dois tamanhos de partícula, que tem demonstrado resultados contraditórios em relação à formação óssea usando partículas pequenas ou grandes. O objetivo desta revisão sistemática e meta-análise é comparar o volume de formação óssea e o volume de enxerto residual em levantamento de seio usando partículas pequenas e grandes. Os seguintes dados foram comparados: volume de formação óssea (%) e volume residual de partículas de enxerto (%) dados por análise histomorfométrica. A seleção inicial resultou em 236 artigos. Após remoção de artigos duplicados e análise dos títulos, resumos e textos completos, três artigos foram incluídos na meta-análise. Os volumes de formação óssea e de enxerto residual não diferenciam entre os tamanhos de partícula pequeno e grande, com baixa heterogeneidade dos artigos. O tamanho de partícula de enxerto ósseo bovino não influencia o percentual de formação óssea; partículas de enxerto ósseo bovino pequenas e grandes apresentaram enxerto residual similar; mais ensaios clínicos randomizados deveriam ser realizados para confirmar que o tamanho de partícula de enxerto não afeta os resultados de levantamento de seio maxilar.

Incorporation of amoxicillin-loaded microspheres in mineral trioxide aggregate cement: an in vitro study.

OBJECTIVES: In this study, we investigated the potential of amoxicillin-loaded polymeric microspheres to be delivered to tooth root infection sites via a bioactive reparative cement. MATERIALS AND METHODS: Amoxicillin-loaded microspheres were synthesized by a spray-dray method and incorporated at 2.5% and 5% into a mineral trioxide aggregate cement clinically used to induce a mineralized barrier at the root tip of young permanent teeth with incomplete root development and necrotic pulp. The formulations were modified in liquid:powder ratios and in composition by the microspheres. The optimized formulations were evaluated in vitro for physical and mechanical eligibility. The morphology of microspheres was observed under scanning electron microscopy. RESULTS: The optimized cement formulation containing microspheres at 5% exhibited a delayed-release response and maintained its fundamental functional properties. When mixed with amoxicillin-loaded microspheres, the setting times of both test materials significantly increased. The diametral tensile strength of cement containing microspheres at 5% was similar to control. However, phytic acid had no effect on this outcome (p > 0.05). When mixed with modified liquid:powder ratio, the setting time was significantly longer than that original liquid:powder ratio (p < 0.05). CONCLUSIONS: Lack of optimal concentrations of antibiotics at anatomical sites of the dental tissues is a hallmark of recurrent endodontic infections. Therefore, targeting the controlled release of broad-spectrum antibiotics may improve the therapeutic outcomes of current treatments. Overall, these results indicate that the carry of amoxicillin by microspheres could provide an alternative strategy for the local delivery of antibiotics for the management of tooth infections.

Nanoneedle-like zinc oxide as a filler particle for an experimental adhesive resin.

AIM: The aim of this study was to develop an experimental adhesive resin with nanoneedle-like zinc oxide (N-ZnO), an inorganic filler, that could avoid particle agglomeration and lead to a homogeneous stress distribution within the material and characterize it. MATERIALS AND METHODS: N-ZnO particles obtained by a thermal evaporation technique were characterized regarding size and surface area and added at 0 (control), 1, 2, 5, and 10 wt%, to an experimental adhesive resin. The following experimental adhesive resins' properties were assessed: radiopacity, contact angle to conditioned enamel and dentin, color, degree of conversion, flexural strength, resistance to degradation, and cytotoxicity. Statistical analysis was performed using one-way ANOVA and Tukey's post hoc test and paired Student's t-test. RESULTS: Particles presented a mean particle size of 40 nm and a specific surface area of 16 m2/g. N-ZnO10%showed an increased radiopacity when compared to N-ZnO0%. Contact angles were significantly higher for N-ZnO10%at enamel and N-ZnO2%, N-ZnO5%, and N-ZnO10%at dentin. All groups showed color change when compared to N-ZnO0%. Higher the N-ZnO concentration, lower the degree of conversion. There were no significant differences between the groups for flexural strength and resistance to degradation. The addition of N-ZnO showed no difference in cytotoxicity when compared to positive control, N-ZnO0%, and all groups showed higher values than negative control. CONCLUSIONS: N-ZnO possibly exceeded potential limitations due to particles' agglomeration and improved the transference and distribution of stress within the material. It could be effectively used as a filler for adhesive resins.

Effect of immersion in various disinfectant solutions on the properties of a heat-cured acrylic resin / Efeito da imersão em diferentes soluções desinfetantes nas propriedades de uma resina acrílica de termoativação

ABSTRACT Objective: The aim of the present study was to evaluate the influence, of immersion in different disinfectant solutions, on microhardness and surface roughness of a heat-cured acrylic resin. Methods: Specimens were immersed in distilled water, commercial vinegar for domestic use, sodium hypochlorite and hydrogen peroxide, for 150 hours or 300 hours (n=10). After periods of immersion, Knoop microhardness and surface roughness were evaluated using a microhardness tester and a roughness tester, respectively. The data were analyzed using two-way ANOVA and Holm-Sidak, at a level of significance of 5%. Results: The microhardness values ranged from 16.90 ± 0.33 to 17.80 ± 0.51 and roughness values from 0.05 ± 0.01 to 0.08 ± 0.02. There is no difference in microhardness and roughness between groups and times (p>0.05). Conclusion: Within the limitations of this study, it is possible to conclude that vinegar and hydrogen peroxide, as alternative disinfectant solutions for acrylic resin devices, did not promote deleterious effects on microhardness and polishing of a heat-cured acrylic resin used for the fabrication of prostheses, neither in the medium term nor the long term.

RESUMO Objetivo: Avaliar a influência da imersão em diferentes soluções desinfetantes na microdureza e rugosidade de uma resina acrílica de termoativação. Métodos: Corpos de prova de resina acrílica termopolimerizável foram imersos em água destilada, vinagre comercial de uso doméstico, hipoclorito de sódio e peróxido de hidrogênio, por períodos de 150 h ou 300 h (n=10). A microdureza Knoop e a rugosidade superficial dos corpos de prova foram avaliadas com o uso de microduro?metro e rugosímetro, respectivamente. Os dadosforam analisados com o teste análise de variância a dois critérios e Holm-Sidak, com nível de significância de 5%. Resultados: Osvalores de microdureza variaram de 16,90 ± 0,33 a 17,80 ± 0,51 e a rugosidade, de 0,05 ± 0,01a 0,08 ± 0,02. Não houve diferença nos resultados de microdureza e rugosidade entre os grupos e tempos (p>0.05). Conclusão: Dentro das limitações do estudo, é possível concluir que a utilização de vinagre ou de peróxido de hidrogênio, como alternativas para a desinfecção de resina acrílica, não provocam efeitos deletérios na dureza e no polimento da resina acrílica termoativada utilizada para confecção de próteses, nem a médio nem a longo prazo.

Performance of progressive and constant tapered instruments rotary systems at canal preparation / Desempenho de sistemas endodônticos rotatórios constante e progressivo no preparo do canal radicular

ABSTRACT Objective: The aim of this study was to compare the performance of two nickel-titanium rotary systems regarding the preparation time, final shape of canal, incidence of aberration, transportation, and fracture of instrument. Methods: A total of 40 simulated canals in resin blocks with 30o curves and a length of 17 mm were divided randomly into two groups: preparation with ProTaper and BioRaCe systems up to F5 and BR5 respectively. Pre- and post-operative canal images were taken and superimposed in order to identify aberrations, transportation, and to take measurements of the canal width. In addition, the preparation time and instrument fractures were recorded. The data were analyzed using Student's t test. Results: There is no difference (p>.05) comparing the systems regarding preparation time, canal aberration, and instrument fracture rates. The progressive tapered instruments of ProTaper prepared significantly larger canal widths in the apical third (p<.05). Conclusion: Overall, both systems provided safe canal preparation, associated with few canal aberrations and instrument fractures.

RESUMO Objetivo: Comparar o desempenho de dois sistemas rotatórios em relação ao tempo de preparo, formato final e alterações do canal, desvio e fratura de instrumento. Métodos: Um total de 40 canais simulados em blocos de resina com curvatura de 30o e comprimento de 17 mm foram divididos randomicamente nos sistemas ProTaper e BioRaCe preparados até F5 e BR5 respectivamente. Imagens pré e após o preparo dos canais foram obtidas e superpostas para identificação de alterações de forma, desvios e largura. O tempo de preparo e fratura de instrumentos também foram avaliados. Os dados foram analisados por teste t de Student. Resultados: O tempo de preparo, alterações de forma e taxa de fratura de instrumentos não teve diferença entre os dois sistemas avaliados (p>0,05). Os instrumentos progressivos do ProTaper resultou em canais significativamente mais largos no terço apical (p<0,05). Conclusão: Os dois sistemas rotatórios avaliados resultaram em preparo endodôntico seguro, com poucas alterações e fratura de instrumento.

Enamel Roughness Changes after Removal of Orthodontic Adhesive.

The aim of this study was to evaluate enamel roughness, quality of the enamel surfaces and time duration comparing different orthodontic adhesive removal protocols. Premolars were used to test three adhesive removal methods (n = 20): five-blade carbide bur, 30-blade carbide bur, and ultrasonic diamond bur. Bracket was bonded using TransbondTM XT adhesive. Roughness with different parameters was measured before bracket bonding and after adhesive remnants removal. Micromorphological analysis of enamel surface (n = 5) was performed by SEM images and categorized in enamel damage index-"perfect"; "satisfying"; "imperfect"; and "unacceptable". Time was measured in seconds. All removal methods caused increased roughness in relation to Ra, Rq, and Rz parameters (X axis) comparing to healthy enamel surface. Enamel surface resulted from removal using five-blade burs was scored as satisfactory. Carbide bur groups decreased the roughness values of Ra, Rq, and Rz parameters on the Y axis and enamel surface was considered unacceptable. The 30-blade group increased symmetry (Rsk) and flattening (Rku) parameters of roughness and surface was scored as unsatisfactory. Diamond bur removed adhesive in 54.8 s, faster than five-blade carbide bur. The five-blade bur group resulted in less enamel roughness than the 30-blade and diamond groups.

Effect on adhesion of a nanocapsules-loaded adhesive system.

This study aimed to evaluate the in situ degree of conversion, contact angle, and immediate and long-term bond strengths of a commercial primer and an experimental adhesive containing indomethacin- and triclosan-loaded nanocapsules (NCs). The indomethacin- and triclosan-loaded NCs, which promote anti-inflammatory and antibacterial effects through controlled release, were incorporated into the primer at a concentration of 2% and in the adhesive at concentrations of 1, 2, 5, and 10%. The in situ degree of conversion (DC, n=3) was evaluated by micro-Raman spectroscopy. The contact angle of the primer and adhesive on the dentin surface (n = 3) was determined by an optical tensiometer. For the microtensile bond strength µTBS test (12 teeth per group), stick-shaped specimens were tested under tensile stress immediately after preparation and after storage in water for 1 year. The data were analyzed using two-way ANOVA, three-way ANOVA and Tukey's post hoc tests with α=0.05. The use of the NC-loaded adhesive resulted in a higher in situ degree of conversion. The DC values varied from 75.07 ± 8.83% to 96.18 ± 0.87%. The use of NCs in only the adhesive up to a concentration of 5% had no influence on the bond strength. The contact angle of the primer remained the same with and without NCs. The use of both the primer and adhesive with NCs (for all concentrations) resulted in a higher contact angle of the adhesive. The longitudinal µTBS was inversely proportional to the concentration of NCs in the adhesive system, exhibiting decreasing values for the groups with primer containing NCs and adhesives with increasing concentrations of NCs. Adhesives containing up to 5% of nanocapsules and primer with no NCs maintained the in situ degree of conversion, contact angle, and immediate and long-term bond strengths. Therefore, the NC-loaded adhesive can be an alternative method for combining the bond performance and therapeutic effects. The use of an adhesive with up to 5% nanocapsules containing indomethacin and triclosan and a primer with no nanocapsules maintained the long-term bond performance.

Polymerisation, antibacterial and bioactivity properties of experimental orthodontic adhesives containing triclosan-loaded halloysite nanotubes.

OBJECTIVE: To evaluate the immediate enamel bond strength, in situ degree of conversion and the polymerisation rate of three experimental orthodontic adhesives containing triclosan-loaded halloysite nanotubes. The antibacterial and bioactivity properties of such experimental materials were also assessed. MATERIALS AND METHODS: Three experimental orthodontic adhesives were formulated by incorporating triclosan-loaded halloysite nanotubes (TCN-HNT) at different concentrations (5wt%, 10wt% and 20wt%) into a resin blend (Control). The maximum polymerisation rate of the tested adhesives was evaluated trough FTIR, while Raman was used to analyse the in situ degree of conversion (DC) at the bracket/enamel interface. The shear bond strength (SBS) of the enamel-bonded specimens was assessed at 24h. The antibacterial properties of the experimental materials against S. Mutans were evaluate up to 72h, while, their bioactivity was evaluated after 14days of artificial saliva (AS) storage through SEM-EDS and Raman spectromicroscopy. RESULTS: Incorporation of TCN-HNT increased the polymerisation properties without interfering with the immediate bonding properties of the experimental adhesives. All experimental adhesives containing TCN-HNT inhibited bacterial growth at 24h, and induced mineral deposition after 14days of AS storage. At 72h, only the experimental system containing 20% TCN-HNT maintained such a capability. CONCLUSIONS: Adhesives doped with TCN-HNT present improved polymerisation properties and suitable bonding performance. However, only the adhesives containing TCN-HNT >10% might promote long-term antibacterial activity and reliable mineral deposition. CLINICAL SIGNIFICANCE: The use of adhesives containing triclosan-loaded halloysite represents a promising "smart" approach to bond orthodontic brackets and bands; these might prevent enamel demineralisation and induce enamel remineralisation during the treatment.

Influence of the addition of microsphere load amoxicillin in the physical, chemical and biological properties of an experimental endodontic sealer.

AIM: To develop an endodontic sealer with amoxicillin-loaded microsphere and to evaluate its properties. METHODS: Experimental sealer was obtained by mixing 70wt% UDMA, 15wt% GDMA and 15wt% BISEMA. In addition, CQ, DHEPT and PB were incorporated at 1 mol% and 0.01wt% BHT and 10wt% YbF3. Microspheres were produced by drying in spray dryer. Two experimental groups (10 and 15wt% of microspheres) and one control group (without microspheres) were formulated. The sealers were evaluated for the degree of conversion (n=3), degradation in solvent (n=3), drug release profile (n=3), antimicrobial activity (n=3), flow (n=3), film thickness (n=3) and cytotoxicity (n=3). Data were analyzed by ANOVA and Tukey with significance level of 5%. RESULTS: Microespheres presented a mean size of 2.664µm. Immediate degree of conversion ranged from 51.73% to 55.13% and the 24h degree of conversion ranged from 60.79% to 73.80%. Upon solvent degradation 54.44% and 56.21% reduction in hardness were observed for 10% and 15% concentrations respectivelly. The drug release profile showed an average release of 73.76% of the drug in 96h. Significant reduction in antimicrobial activity was observed for 10% concentration after 24h, 48h and 96h compared to control. The flow and film thickness showed values in accordance to the ISO 6876. Cytotoxicity showed high cellular viability. CONCLUSION: The addition of up to 10% of microspheres containing amoxicillin presented antimicrobial activity and did not alter the properties of the experimental endodontic cement. CLINICAL SIGNIFICANCE: Amoxicillin microspheres with its antimicrobial activity in root canal sealers could reduce reintervations in endodontics when persistent bacteria or reinfection takes place in root canal system.

Effect on adhesion of a nanocapsules-loaded adhesive system

Abstract This study aimed to evaluate the in situ degree of conversion, contact angle, and immediate and long-term bond strengths of a commercial primer and an experimental adhesive containing indomethacin- and triclosan-loaded nanocapsules (NCs). The indomethacin- and triclosan-loaded NCs, which promote anti-inflammatory and antibacterial effects through controlled release, were incorporated into the primer at a concentration of 2% and in the adhesive at concentrations of 1, 2, 5, and 10%. The in situ degree of conversion (DC, n=3) was evaluated by micro-Raman spectroscopy. The contact angle of the primer and adhesive on the dentin surface (n = 3) was determined by an optical tensiometer. For the microtensile bond strength µTBS test (12 teeth per group), stick-shaped specimens were tested under tensile stress immediately after preparation and after storage in water for 1 year. The data were analyzed using two-way ANOVA, three-way ANOVA and Tukey's post hoc tests with α=0.05. The use of the NC-loaded adhesive resulted in a higher in situ degree of conversion. The DC values varied from 75.07 ± 8.83% to 96.18 ± 0.87%. The use of NCs in only the adhesive up to a concentration of 5% had no influence on the bond strength. The contact angle of the primer remained the same with and without NCs. The use of both the primer and adhesive with NCs (for all concentrations) resulted in a higher contact angle of the adhesive. The longitudinal μTBS was inversely proportional to the concentration of NCs in the adhesive system, exhibiting decreasing values for the groups with primer containing NCs and adhesives with increasing concentrations of NCs. Adhesives containing up to 5% of nanocapsules and primer with no NCs maintained the in situ degree of conversion, contact angle, and immediate and long-term bond strengths. Therefore, the NC-loaded adhesive can be an alternative method for combining the bond performance and therapeutic effects. The use of an adhesive with up to 5% nanocapsules containing indomethacin and triclosan and a primer with no nanocapsules maintained the long-term bond performance.

Effect of beverages on surface properties of resin-based sealants

Aim: The aim of this study was to determine degree of conversion of resin-based sealants and the effect of beverages on surface roughness and color change of materials. Methods: Two commercial resin-based sealants were evaluated (Defense Chroma® and BioSeal®). Degree of conversion (DC) was initially measured using Fourier-transformed infrared (FTIR). Specimens of each sealant were maintained in distilled water and immersed one hour daily in grape juice and cola drink for 30 days. One group was maintained only in distilled water, as a control. Surface roughness and color change were measured before immersion, after seven days of immersion and after 30 days of immersion. Results were analyzed using t-test, paired t-test, one-way repeated measures ANOVA, one-way ANOVA and post-hoc tests (0.05 level of significance). Results: There was no significant difference regarding degree of conversion and initial surface roughness comparing both commercial sealants. Surface roughness increased for BioSeal® immersed in cola drink for 30 days. After 30 days, all groups presented significant color change. Conclusions: The effect of beverages on color stability and surface roughness of resin-based sealants depended on exposure time and kind of beverage (AU)

Anti-inflammatory effect of an adhesive resin containing indomethacin-loaded nanocapsules.

OBJECTIVE: To analyze the anti-inflammatory and analgesic effects of an adhesive resin containing indomethacin-loaded nanocapsules in rat model. DESIGN: Adhesive resin disks with or without indomethacin-loaded nanocapsules were subcutaneously implanted into right hind paw of rats. A week after surgical procedure, 2% formalin solution was intradermally injected into plantar surface of paw. Nociceptive and inflammatory responses were evaluated by formalin test. Paw edema by pletismometer and mechanical hyperalgesia by von Frey test were performed on day 2, day 4, day 6, day 8, day 10 and day 12 after surgery. IL-6, IL-10, and lactate dehydrogenase (LDH) serum levels were determined by ELISA-sandwich test. RESULTS: Group containing indomethacin-loaded nanocapsules (NC) presented lower edema in the right hind paw at 24h after formalin injection than those of the control group (CT) (P<0.01). NC group showed decrease in the nociceptive response in phase I (neurogenic pain) compared to CT group (NC - 66.86±22.83s X CT - 130.17±35.83s, P<0.001). NC group presented supporting higher intensity of stimulus on days 8 and 12 (24h and 72h after formalin injection) (P<0.01 and P<0.02 respectively). The IL-6 serum level was also significantly higher in the NC group than CT group (p<0.001). CONCLUSIONS: These results indicate that an adhesive resin containing indomethacin-loaded nanocapsules has anti-inflammatory and nociceptive activities in a chemical model of acute inflammation. The present investigation confirms an adhesive resin with drug-loaded nanocapsules may be useful for improving therapeutic effect for adhesives to be used in deep cavities.

Antimicrobial effect and physicochemical properties of an adhesive system containing nanocapsules.

OBJECTIVE: To incorporate indomethacin and triclosan-loaded nanocapsules into primer and adhesive, and evaluate its properties. METHODS: Indomethacin and triclosan were encapsulated by deposition of preformed polymer and subsequently characterized regarding morphology, particle size, drug content and cytotoxicity. Nanocapsules (NCs) were incorporated into primer at 2% and into adhesive at 1, 2, 5, and 10% concentrations. Degree of conversion (DC) and softening in ethanol of the adhesive were evaluated. Drug release and drug diffusion through dentin was quantified by high performance liquid chromatography. Antimicrobial test was performed until 96h. RESULTS: Spherical and biocompatible NCs presented mean size of 159nm. Drugs content was 3mg indomethacin/g powder and 2mg triclosan/g powder. Incorporating NCs in adhesive showed no influence in DC (p=0.335). The addition of 2% of NCs showed no influence in softening in ethanol (p>0.05). After 120h, 93% of indomethacin and 80% of triclosan were released from primer, 20% of indomethacin and 17% of triclosan were released from adhesive with 10% of NCs. Indomethacin showed diffusion through dentin. In 24h, adhesive containing 2 and 5% of NCs using primer with NCs showed antimicrobial effect. In 96h, adhesives containing different concentration of NCs promoted antimicrobial effect. CONCLUSIONS: Indomethacin and triclosan-loaded nanocapsules were successfully incorporated into primer and adhesive, promoting controlled drugs release, indomethacin diffusion through dentin and antimicrobial effect without compromising its physicochemical properties. SIGNIFICANCE: Indomethacin and triclosan-loaded nanocapsules have potential to prevent recurrent caries and to be used in deep cavities controlling pulpar inflammatory process.

Effect of indomethacin-loaded nanocapsules incorporation in a dentin adhesive resin.

OBJECTIVES: The aim of this study was to produce indomethacin-loaded nanocapsules (IndOH-NCs) and evaluate the influence of their incorporation into an adhesive resin. MATERIALS AND METHODS: Indomethacin was encapsulated by the deposition of preformed polymer. IndOH-NCs were characterized by laser diffractometry, Fourier transformed infrared spectrometry, transmission electron microscopy (TEM), scanning electron microscopy, high-performance liquid chromatography (HPLC), and MTT assay. Nanocapsules (NCs) were incorporated into an adhesive in concentrations of 1, 2, 5, and 10 %. The addition was visualized by TEM and drug release was evaluated by HPLC until 120 h of immersion in simulated body fluid (SBF). Drug diffusion through dentin was tested using a Franz diffusion cell apparatus and quantified by HPLC. The degree of conversion (DC), softening in ethanol, and microtensile bond strength (µTBS) were evaluated to determine whether the nanocapsules influenced the adhesive. Data were analyzed using one-way ANOVA and Tukey's post hoc test for DC, softening in ethanol, µTBS, and cytotoxicity, and paired t test for comparison between the initial and final Knoop microhardness. RESULTS: IndOH-NCs, with a spherical shape and a mean diameter of 165 nm, were incorporated into an adhesive. Indomethacin content was 7 mg drug/g powder. IndOH-NCs maintained high cell viability. At 120 h, an amount of 13.83 % of indomethacin was released, and after 7 days, 7.07 % of this drug was diffused through dentin for an adhesive containing 10 % of nanocapsules. No alteration in the DC, softening in ethanol, and µTBS resulted from NC addition. CONCLUSIONS: IndOH-NCs may be incorporated into adhesive systems, without compromising properties, to add an anti-inflammatory drug controlled release for restorative procedures in deep cavities. CLINICAL SIGNIFICANCE: Here is the first step toward the goal of providing agents to act at an inflammatory process of pulp tissue through dental adhesives via encapsulation of drug.

Tecnologias de informação e comunicação na educação da Odontologia: estudo transversal de uma população do sul do Brasil / Information and Communication Technologies in dental education: cross-sectional study of a population of southern Brazil

O objetivo do presente estudo foi avaliar as competências em relação às Tecnologias de Informação e Comunicação (TICs) de estudantes de Odontologia. Um estudo transversal foi realizado com os estudantes de Odontologia da Universidade Federal do Rio Grande do Sul, Brasil. Os dados foram coletados através de um questionário previamente validado pelo Centro de Ciências de Saúde Oral da Universidade de Malmö e submetido ao processo de adaptação transcultural para o português. Os resultados foram transformados em escores conforme literatura prévia e categorizados para as comparações. Análise descritiva, qui-quadrado e teste exato de Fischer foram utilizados. O escore de competência em relação às TICs foi considerado muito bom e apresentou relação com o nível de escolaridade materno. Já o escore de importância das TICs foi mediano e relacionado à idade. Concluiu-se que os estudantes de Odontologia apresentaram bom domínio das ferramentas de TICs e nível moderado em relação à importância atribuída ao uso odontológico dessas tecnologias (AU).

The purpose of the present study was to evaluate the competence of the students to use technologies in dental educational. A cross-sectional study was done with dental students of a university of the south of Brazil. It was used a questionnaire previously validated by the Center Oral Health Sciences of University of Malmö (Sweden) and adapted to Portuguese. The collected data were transformed into scores based on Mattheos et al. (2005). For analysis purposes, scores and sociodemographic variables were categorized. The descriptive analyses was realized, Chi Square and Exact Fischer`s tests were used to test the association between the sociodemographic data and the scores regarding the Information and Communication Technologies (ICT). The mean competence score was considered very good and associated with education level of the mothers. The mean importance score was regular and associated with age. It was concluded that the students of a university of south of Brazil had a very good level regarding the competence of the use of ICT even though moderate level in relation to the importance was given to dental use of these technologies (AU).

Diagnostic challenge of a deep minor salivary gland neoplasm.

Core needle biopsy represents a safe and cheap alternative diagnostic method to open biopsy and fine-needle aspiration cytology in head and neck tumors. There is little evidence in the literature about the use of core needle biopsy in minor salivary gland lesions. This single case report presents a 60-year-old woman with a painless swelling in the soft palate, breathing and swallowing difficulties, and a feeling of suffocation. Two open biopsies had inconclusive diagnosis and the lesion could only be assessed and diagnosed as pleomorphic adenoma through core needle biopsy. Recognizing the correct indication of core needle biopsy can benefit both health professionals and patients; thus, it is important to consider the possibility of performing this method to diagnose minor salivary gland tumors.

Bismuth subsalicylate as filler particle for an experimental epoxy-based root canal sealer

AIM: To evaluate the influence of bismuth subsalicylate addition in different concentrations on theproperties ofan experimental epoxy-based root canal sealer. METHODS: Bismuth subsalicylate in 20%, 40%, 60%, 80%, 100% and 120 wt% was added tothe sealer. Flow, film thickness, working time, setting time, dimensional change, sorption, solubility and cytotoxicity were evaluated according to ISO standard. Data were statistically analyzed by one-way ANOVA and Tukey'stest with a significance level of 5% for all tests. RESULTS:The flow, working and setting times significantly decreased withincreasing particle concentration. The film thickness, dimensional change, water sorption and solubility values significantly increased with higher particle amount. The results for cytotoxicity showed no statistically significant differences among the particle proportions. CONCLUSIONS: The results suggest that the addition up to 80% wt of bismuth subsalicylate appears to be a promising filler particle to root canal sealer development.

Banco de dentes humanos para o ensino e pesquisa em Odontologia / Human teeth bank for education and research in Dentistry

O uso de dentes humanos para o ensino e pesquisa em Odontologia é uma prática freqüente. A implantação de Bancos de Dentes Humanos (BDH) em instituições de ensino é fundamental para viabilizar a manipulação segura para aprendizagem, pesquisa e inovações tecnológicas que façam uso de dentes humanos. Para que seu funcionamento seja adequado, a organização e a legalização do uso de dentes devem ser divulgadas. Procedimentos relativos às etapas de arrecadação, limpeza e desinfecção, separação e armazenamento, cessão e/ou empréstimo e de biossegurança devem ser desenvolvidos, aprimorados e colocados ao alcance dos interessados. Este artigo tem como objetivo fazer um levantamento do número de BDH em instituições de ensino de Odontologia do Estado do Rio Grande do Sul e buscar na literatura orientações disponíveis sobre os aspectos práticos, legais, técnicos e científicos necessários ao seu funcionamento em instituições de ensino e pesquisa em Odontologia.

The use of human teeth for teaching/education and research in dentistry is a common practice. The establishment of Human Teeth Bank (BDH) in institutions of education is essential to enable the safe handling in teaching, research and the discovery of new technologies which make use of human teeth. Before BDH establishment is appropriate, its organization and legalization must be disclosed. Procedures of collection, cleaning and disinfection, separation and storage, disposal and/or loan and biosecurity should be developed and improved. The aim of this study is to search the number of BDH inside schools of Dentistry units at Rio Grande do Sul state and to review the literature about the importance of BDH in institutions of education and research as well as its legal, technical and scientific aspects.